Ryton® R-4-200NA PPS连接器
Ryton® R-4-200NA and R-4-200BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and low maintenance molding using conventional molding equipment
| Availability | Asia Pacific Europe Latin America North America |
| Filler / Reinforcement | Glass Fiber, 40% Filler by Weight |
| Features | Good Strength |
| Uses | Automotive Applications |
| RoHS Compliance | RoHS Compliant |
| Appearance | Natural Color |
| Forms | Pellets |
| Processing Method | Injection Molding |
| 物理性能 | 名义价值 | 单位 | 测试方法 |
| 密度 / 比重 | 1.68 | g/cm³ | ASTM D792 |
| 模塑收缩率 4 | 内部方法 | ||
| 流动方向 : 3.20 mm | 0.20 | % | |
| 横向流动 : 3.20 mm | 0.50 | % | |
| 吸水率 | |||
| 24小时 | 0.020 | % | ASTM D570 |
| 24小时，23°C | 0.030 | % | ISO 62 |
| 饱和，23°C | 0.26 | % | 内部方法 |
| 平衡，23°C，50% RH | 0.25 | % | 内部方法 |
| 机械的 | 名义价值 | 单位 | 测试方法 |
| 拉伸模量 | 15700 | MPa | ISO 527-1 |
| 拉伸应力 | |||
| -- | 200 | MPa | ISO 527-2 |
| -- | 193 | MPa | ASTM D638 |
| -- 5 | 194 | MPa | ISO 527-2 |
| 拉伸应变 | |||
| 断裂 | 1.7 | % | ISO 527-2 |
| 断裂 | 1.6 | % | ASTM D638 |
| 断裂 5 | 1.8 | % | ISO 527-2 |
| 弯曲模量 | |||
| -- | 14500 | MPa | ASTM D790 |
| -- | 14000 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 285 | MPa | ISO 178 |
| -- | 269 | MPa | ASTM D790 |
| 抗压强度 | 275 | MPa | ASTM D695 |
| 抗剪强度 | 96.0 | MPa | ASTM D732 |
| 泊松比 | 0.40 | | ISO 527 |