TOPAS® 5013F-04 COC高流动性
TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food applications. It is used in monolayer cast blends, and in coextruded blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS.
Selected Applications
Decorative film and sheet
General packaging
Food packaging
Blown film
Food contact
Leading Attributes
Gloss, hardness, chemical resistance, forming
Easy or linear tear, heat resistance, hot fill, gloss
Not manufactured with BPA, phthalates, or halogens
High strength and high productivity
Broad regulatory compliance
Related Grades for Packaging and Film Extrusion
TOPAS 6013F-04 - high temperature grade with standard flow
| 可用性 | 非洲与中东 亚太地区 欧洲 拉丁美洲 北美洲 |
| 特性 | 无定形 不含双酚A 耐化学品 共聚物 可接触食品 无卤 高透明度 高流动性 高光泽度 高纯度 高刚性 高强度 防潮层 |
| 用途 | 混合 薄膜 食品包装 包装 片材 |
| 机构认证 | EU 10/2011 FDA FCN 405 |
| 表单 | 颗粒 |
| 处理方法 | 吹膜 流延膜 共挤薄膜 薄膜挤出 热成型 |
| 物理 | 标称值 | 单位 | 测试方法 |
| 密度 | 1.02 | g/cm³ | ISO 1183 |
| 熔体质量流动速率 (MFR) | 计算值 | ||
| 190°C/2.16 kg | < 0.10 | g/10 min | |
| 230°C/2.16 kg | 8.0 | g/10 min | |
| 熔体体积流速 (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | < 0.10 | cm³/10min | |
| 230°C/2.16 kg | 9.0 | cm³/10min | |
| 吸水率(饱和，23°C) | 0.010 | % | ISO 62 |
| 薄膜 | 标称值 | 单位 | 测试方法 |
| 拉伸模量 | ISO 527-3 | ||
| MD : 70 µm, 流延膜 | 2620 | MPa | |
| TD : 71 µm, 流延膜 | 2480 | MPa | |
| 拉伸应力 | ISO 527-3 | ||
| MD : 断裂，70 µm，流延膜 | 35.2 | MPa | |
| TD : 断裂，70 µm，流延膜 | 24.8 | MPa | |
| 拉伸伸长率 | ISO 527-3 | ||
| MD : 断裂，70 µm，流延膜 | 1.4 | % | |
| TD : 断裂，70 µm，流延膜 | 1.1 | % | |
| Dart 掉落冲击(70 µm, 浇延薄膜) | < 36 | g | ISO 7765-1 |
| Elmendorf 撕裂强度 | ISO 6383-2 | ||
| MD : 70 µm, 流延膜 | 0.11 | N | |
| TD : 70 µm, 流延膜 | 0.11 | N | |
| 氧气透过率(23°C, 70 µm, 流延膜, 50% RH) | 24 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| 水蒸气透过率(70 µm, 38°C, 流延膜, 90% RH) | 0.098 | g·mm/m²/atm/24 hr | ISO 15106-3 |
| 热 | 标称值 | 单位 | 测试方法 |
| 玻璃化转变温度 | 134 | °C | ISO 11357-2 |
| 光学 | 标称值 | 单位 | 测试方法 |
| 光泽(60°，70.0 µm，流延膜) | > 100 | | ISO 2813 |
| 雾度(70.0 µm, 流延膜) | < 1.00 | % | ISO 14782 |
| TOPAS® 8007F-04 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007F-600 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007F-600 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007S-04 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007S-04 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007X10 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007X10 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 9506F-500 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 9506F-500 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® Blend 16-024 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® Elastomer E-140 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® Elastomer E-140 | Daicel | Cyclic Olefin Copolymer (COC) |