TOPAS® 6013F-04 COC高刚性
TOPAS 6013F-04 is a high temperature, general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food applications. It is used in monolayer and blended cast applications, and in coextrusions and blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS.
Selected Applications
| 可用性 | 非洲与中东 亚太地区 欧洲 拉丁美洲 北美洲 |
| 用途 | 混合 流延膜 薄膜 食品包装 通用 包装 药品包装 片材 |
| 机构评级 | DMF 12132 EU 10/2011 FDA FCN 405 ISO 10993 USP Class VI |
| 表格 | 颗粒 |
| 处理方法 | 吹膜 流延膜 共挤膜 薄膜挤出 热成型 |
| 物理 | 名义价值 | 单位 | 测试方法 |
| 密度 | 1.02 | g/cm³ | ISO 1183 |
| 熔体质量流动速率 (MFR) | 已计算 | ||
| 190°C/2.16 kg | < 0.10 | g/10 min | |
| 230°C/2.16 kg | 0.90 | g/10 min | |
| 熔体体积流量 (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | < 0.10 | cm³/10min | |
| 230°C/2.16 kg | 1.0 | cm³/10min | |
| 吸水率（饱和状态，23°C） | 0.010 | % | ISO 62 |
| 薄膜 | 名义价值 | 单位 | 测试方法 |
| 拉伸模量 | ISO 527-3 | ||
| MD : 70 µm, 流延薄膜 | 2410 | MPa | |
| TD : 70 µm，流延膜 | 2280 | MPa | |
| 拉伸应力 | ISO 527-3 | ||
| MD : 断裂，70 µm，流延膜 | 55.2 | MPa | |
| TD : 断裂，70 µm，流延膜 | 44.8 | MPa | |
| 拉伸伸长率 | ISO 527-3 | ||
| MD : 断裂，70 µm，流延膜 | 2.4 | % | |
| TD : 断裂，70 µm，流延膜 | 2.2 | % | |
| 镖枪冲击强度(70 µm, 浇延薄膜) | < 36 | g | ISO 7765-1 |
| Elmendorf撕裂强度 | ISO 6383-2 | ||
| MD : 70 µm, 流延薄膜 | 0.088 | N | |
| TD : 70 µm，流延膜 | 0.088 | N | |
| 氧气透过率(23°C, 70 µm, 流延膜, 50% RH) | 28 | cm³·mm/m²/atm/24 小时 | ASTM D3985 |
| 水蒸气透过率(70 µm, 38°C, 流延膜, 90% RH) | 0.13 | g·mm/m²/atm/24 小时 | ISO 15106-3 |
| TOPAS® 8007F-04 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007F-600 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007F-600 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007S-04 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007S-04 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007X10 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 8007X10 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 9506F-500 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® 9506F-500 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® Blend 16-024 | Daicel | Cyclic Olefin Copolymer (COC) | |
| TOPAS® Elastomer E-140 | Topas Advanced Polymers GmbH | Cyclic Olefin Copolymer (COC) | |
| TOPAS® Elastomer E-140 | Daicel | Cyclic Olefin Copolymer (COC) |