TOPAS® 8007F-600 COC薄膜
TOPAS 8007F-600 is a new robust film extrusion grade designed for blending with polyethylene (PE). It is an improved clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include formed PE and PP sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended.
Selected Applications
| 可用性 | 非洲与中东 亚太地区 欧洲 拉丁美洲 北美洲 |
| 功能 | 无定形 不含双酚A 耐化学腐蚀 共聚物 食品接触级 通用用途 良好的韧性 无卤 高光泽 高纯度 高收缩率 高刚性 中等清晰度 防潮阻隔 |
| 用途 | 混合 流延膜 薄膜 食品包装 通用 标签 多层薄膜 包装 片材 |
| 机构评级 | DMF 12132 EU 10/2011 FDA FCN 405 |
| 表格 | 颗粒 |
| 处理方法 | 吹膜 流延膜 薄膜挤出 热成型 |
| 物理的 | 标称值 | 单位 | 测试方法 |
| 密度 | 1.01 | g/cm³ | ISO 1183 |
| 熔体质量流量 (MFR) | 计算值 | ||
| 190°C/2.16 kg | 1.8 | g/10 min | |
| 230°C/2.16 kg | 11 | g/10 min | |
| 熔体体积流量 (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 2.0 | cm³/10min | |
| 230°C/2.16 kg | 12 | cm³/10min | |
| 吸水率（饱和状态，23°C） | 0.010 | % | ISO 62 |
| 薄膜 | 标称值 | 单位 | 测试方法 |
| 拉伸模量 | ISO 527-3 | ||
| MD : 70 µm, 流延薄膜 | 2070 | MPa | |
| TD : 70 µm，流延膜 | 1720 | MPa | |
| 拉伸应力 | ISO 527-3 | ||
| MD : 断裂，70 µm，流延膜 | 55.2 | MPa | |
| TD : 断裂，70 µm，流延膜 | 50.3 | MPa |